| DC Field | Value | Language |
|---|
| dc.contributor.author | Ярмолич, М. В. | - |
| dc.contributor.author | Каланда, Н. А. | - |
| dc.contributor.author | Демьянов, С. Е. | - |
| dc.contributor.author | Гурский, А. Л. | - |
| dc.contributor.author | Ковалев, Л. В. | - |
| dc.contributor.author | Галяс, А. И. | - |
| dc.date.accessioned | 2016-05-20T06:56:48Z | - |
| dc.date.accessioned | 2017-07-13T06:33:09Z | - |
| dc.date.available | 2016-05-20T06:56:48Z | - |
| dc.date.available | 2017-07-13T06:33:09Z | - |
| dc.date.issued | 2016 | - |
| dc.identifier.citation | Ярмолич, М. В. Магнетизм в наноразмерных порошках ферромолибдата стронция = Magnetism in the nanosized strontium ferromolybdate / М. В. Ярмолич [и др.] // Доклады БГУИР. – 2016. – № 3 (97). – С. 63–68. | ru_RU |
| dc.identifier.uri | https://libeldoc.bsuir.by/handle/123456789/6892 | - |
| dc.description.abstract | Цитрат-гель методом при pH = 4, 6, 9 были получены однофазные наноразмерные порошки
Sr2FeMoO6- с различной степенью сверхструктурного упорядочения катионов Fe3+ и Mo5+.
Согласно данным рентгеновской фотоэлектронной спектроскопии, в полученных порошках
Sr2FeMoO6- установлено смешанное валентное состояние катионов железа и молибдена, при
котором с увеличением рН концентрация Fe2+ растет, а концентрация Fe+3 падает. Согласно
данным температурных зависимостей намагниченностей, выполненных в ZFC и FC режимах
в порошках ферримагнетика Sr2FeMoO6-, установлено нестабильное суперпарамагнитное
состояние при Т < 19 К. Обнаружено, что внешнее магнитное поле стимулирует переход в наноразмерных зернах из метастабильного суперпарамагнитного состояния в стабильное выше некоторого значения индукции магнитного поля, превышающей по величине минимальное поле анизотропии. При этом в порошках при pH = 4, количество
наноразмерных зерен больше, чем в pH = 6, 9, что обусловило их большую намагниченность
при Т = (4,2–19) K. | ru_RU |
| dc.language.iso | ru | ru_RU |
| dc.publisher | БГУИР | ru_RU |
| dc.subject | доклады БГУИР | ru_RU |
| dc.subject | ферромолибдат стронция | ru_RU |
| dc.subject | цитрат-гель метод | ru_RU |
| dc.subject | сверхструктурное упорядочение катионов | ru_RU |
| dc.subject | намагниченность | ru_RU |
| dc.subject | strontium ferromolybdate | ru_RU |
| dc.subject | citrate-gel method | ru_RU |
| dc.subject | superstructural ordering | ru_RU |
| dc.subject | redistribution of the electron density | ru_RU |
| dc.subject | magnetization | ru_RU |
| dc.subject | superparamagnetic state | ru_RU |
| dc.title | Магнетизм в наноразмерных порошках ферромолибдата стронция | ru_RU |
| dc.title.alternative | Magnetism in the nanosized strontium ferromolybdate | ru_RU |
| dc.type | Article | ru_RU |
| local.description.annotation | Single-phase nanosized Sr2FeMoO6-δ powders were synthesized by citrate-gel method at pH = 4, 6, 9, with various degrees of superstructural ordering of Fe3+ and Mo5+ cations (P = 65 % for pH = 4, P = 51 % for pH = 6 and P = 20 % for pH = 9). According to the XPS analysis results, mixed
valence state of cations iron and molybdenum was established. With increasing of pH, the Fe2+
concentration value rises from 63 % to 72 %, whereas the Fe+3 concentration drops from 37 % to 28 %.
According to the results of investigations of magnetization temperature dependence performed in ZFC
(zero-field cooling) and FC (field cooling) modes a metastable superparamagnetic state in low-dimensional grains of Sr2FeMoO6- ferrimagnetic powders at T < 19 K was established. In powders with pH = 4 the number of low dimensional grains is significantly larger than powders with pH = 6 and 9.
This has led to their large magnetization value at T = (4,2–19) K. | - |
| Appears in Collections: | №3 (97)
|