Title: Автоэмиссионные характеристики массивов углеродных нанотрубок на локализованных в порах анодного оксида алюминия металло-оксидных столбиках титана
Other Titles: Field emission behaviour of carbon nanotubes embedded into anodic alumina pores on metal oxide catalists
Authors: Соловей, Д. В.
Сахарук, В. Н.
Горох, Г. Г.
Keywords: доклады БГУИР;автоэлектронная эмиссия;анодный оксид алюминия;углеродные нанот­рубки;ориентированные массивы;металло-оксидные наноструктуры
Issue Date: 2008
Publisher: БГУИР
Citation: Соловей, Д. В. Автоэмиссионные характеристики массивов углеродных нанотрубок на локализованных в порах анодного оксида алюминия металло-оксидных столбиках титана = Field emission behaviour of carbon nanotubes embedded into anodic alumina pores on metal oxide catalists / Д. В. Соловей, В. Н. Сахарук, Г. Г. Горох // Доклады БГУИР. – 2008. – № 5 (35). – С. 42–49.
Abstract: Разработан процесс создания массивов вертикально ориентированных углеродных нанотрубок методом химического газофазного осаждения на металло-оксидных нанокатализаторах в порах модифицированной матрицы анодного оксида алюминия. Проведены интегральные автоэмиссионные исследования созданных структур в постоянном и импульсном режимах, локальные исследования отдельных катодов, рассчитаны пороговые напряженности электрического поля и коэффициенты усиления электрического поля р.
Alternative abstract: Thin nanoporous alumina films were grown on n-type Si wafers by anodizing sputtereddeposited Al/Ti layers to prepare matrix of metal oxide catalysts with contact interface -TiC^/Ti/n-Si for later synthesis of carbon nanotubes (CNTs) in the alumina pores. CNTs were grown by CVD in the presence of ferrocene catalyst. Measurements of field emission properties o f the CNTs in anodic alumina were performed in the direct and pulsed current modes. Typical IMLS images of the unstructured samples (about 20 mm2 size, 300-pm electrode gap) showed many emission sites along the edge but only few sites in the specimen’s center, thus corresponding to the distribution o f CNTs in the PAA matrixes. The onset voltage and the field enhancement factor p were calculated for each mode. The carbon nanotubes in the PAA matrixes with TiCVTi/n-Si contact interfaces showed stable electron emission at relatively low field levels. We have strong edge emission demonstrated in IMLS and FESM investigations.
URI: https://libeldoc.bsuir.by/handle/123456789/31825
Appears in Collections:№5 (35)

Files in This Item:
File Description SizeFormat 
Solovey_Avtoemisionnyye.PDF402.18 kBAdobe PDFView/Open
Show full item record Google Scholar

Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.