https://libeldoc.bsuir.by/handle/123456789/48920| Title: | Биоактивные покрытия на основе оксидов титана и тантала для титановых имплантатов |
| Other Titles: | Bioactive coatings based on titanium and tantalum oxides for titanium implants |
| Authors: | Багаев, С. И. Смягликов, И. П. Лазарук, С. К. Купреева, О. В. |
| Keywords: | публикации ученых;имплантаты;кальций-фосфатное покрытие;биоактивные свойства;implant;calcium phosphate coating;bioactive properties |
| Issue Date: | 2021 |
| Publisher: | ФТИ НАН Беларуси |
| Citation: | Багаев, С. И. Биоактивные покрытия на основе оксидов титана и тантала для титановых имплантатов=Bioactive coatings based on titanium and tantalum oxides for titanium implants / С. И. Багаев [и др.] // Современные методы и технологии создания и обработки материалов : сборник научных трудов : в 2 кн. / Физико-технический институт Национальной академии наук Беларуси. – Минск : ФТИ НАН Беларуси, 2021. – Кн. 1. – С. 250-263. |
| Abstract: | Приведены результаты экспериментальных исследований морфологии и свойств биоактивных покрытий, формируемых электрохимическими способами на титановых имплантатах, в виде электретных покрытий на основе оксидов тантала и оксидных покрытий, с высоким содержанием кальция и фосфора. Показано, что электретный заряд в покрытии сохраняется на протяжении не менее 90 дней и характеризуется средней плотностью заряда 4,4•10–4 Кл/м2. Кальций-фосфатные покрытия характеризуются поверхностной пористостью 5–15 %, размерами пор – 0,3–9,4 мкм, отношением концентраций Ca/P – 0,7–2,0, шероховатостью поверхности Ra до 1,7–1,9 мкм в зависимости от режимов плазменно-электролитической обработки. Введение в состав оксидного покрытия танталовых соединений снижает коррозионный ток более чем на порядок. |
| Alternative abstract: | The results of experimental studies of the morphology and properties of bioactive
coatings formed by electrochemical methods on titanium implants, in the form of electret
coatings based on tantalum oxides and oxide coatings with a high content of calcium and
phosphorus, are presented. It is shown that the electret charge in the coating is maintained for
at least 90 days and is characterized by an average charge density of 4.4·10 –4 C/m 2 . Calcium
phosphate coatings are characterized by a surface porosity of 5–15 %, pore size – 0.3–
9.4 µm, Ca/P concentration ratio –0.7–2.0, surface roughness Ra up to 1.7–1.9 µm, depending on conditions of plasma electrolytic treatment. The introduction of tantalum compounds into
the oxide coating reduces the corrosion current by more than an order of magnitude. The results of experimental studies of the morphology and properties of bioactive coatings formed by electrochemical methods on titanium implants, in the form of electret coatings based on tantalum oxides and oxide coatings with a high content of calcium and phosphorus, are presented. It is shown that the electret charge in the coating is maintained for at least 90 days and is characterized by an average charge density of 4.4·10 –4 C/m 2 . Calcium phosphate coatings are characterized by a surface porosity of 5–15 %, pore size – 0.3– 9.4 µm, Ca/P concentration ratio –0.7–2.0, surface roughness Ra up to 1.7–1.9 µm, depending on conditions of plasma electrolytic treatment. The introduction of tantalum compounds into the oxide coating reduces the corrosion current by more than an order of magnitude. |
| URI: | https://libeldoc.bsuir.by/handle/123456789/48920 |
| Appears in Collections: | Публикации в изданиях Республики Беларусь |
| File | Description | Size | Format | |
|---|---|---|---|---|
| Bagayev_Bioaktivnyye.pdf | 5.77 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.